Description
Three-layer cross-oriented strand boards, OSB type 3 of 10 mm
thick, were industrially manufactured from a mixture of wood
species including 50% softwoods, 25% beech, and 25% low hardwoods,
using a continuous press line. The effects of line speed and press
factor on physical and mechanical properties of OSB/3 (exterior
grade) were evaluated, keeping nearly constant the face-core
adhesive ratio. The manufactured boards were classified into five
groups depending on the pressing parameters. The experimental
results showed that all mechanical properties increased, with
increasing press factor and decreasing line speed. The ratios of
bending strength (MOR) and the modulus of elasticity (MOE) parallel
to perpendicular were 1.73 to 1.89 and 2.18 to 2.24, respectively.
No significant differences in thickness swell and water absorption
were observed. The lowest density was achieved at higher speed,
although there was no large variation in densities between groups.
Thickness swelling and internal bond after boil test exceeded the
EN 300 standard requirements for OSB/3 moisture resistance,
excepting a few boards. The results revealed that a correlation
between speed and press factor is necessary in order to improve
mechanical properties and to keep the physical performance of
boards within a limited range of values.
The 300~1500m³/day particle board production line uses raw material
through chips preparation, flakes preparation, dring and sitfting,
glue dosing system, forming and hot pressing, cooling &trimming
and sanding section to make particle board / chipboard. The final
size can be 4 x 8, 6 x 8, 6 x 9, 4 x 12, 6 x 12, 6 x 18. The
particle board has homogeneous structure, smooth surface, good
machining specification and manufacture performance. It is the
ideal substitute of nature wood.
Summary of process flow
- Chips Preparation Section
- Flakes Preparation Section
- Drying and Sifting Section
- Glue Dosing System
- Forming Line
- Continuous Press System
- Master Board Handling System
- Automatic Storage System
- Sanding and Cut-to-size Section
- Surface Grading System
- Automatic Package Section
Main technical data
| Item | Unit | Specification |
| Capacity | m³/d | 300~1500 |
| Width of production line | feet | 4,6,7,8,9 |
| Final board thickness | mm | 6~40 |
| Final board width | mm | 915~2800 |
| Final board length | mm | 1830~5490 |
| Press speed | mm/s | Max. 2000 |
Key equipment of production line
1 High energy efficiency and waste energy can be recycled to save
energy
2 More safe due to low oxygen drying to prevent fire
3 Flaker shape will be well maintained
4 Stable flaker moisture
5 Large unit capacity
1 Large capacity and good performance
2 Frame screen box makes strong and durable
3 Brilliant elastic vibration support
4 Perfect rotary balance technology
5 Self-clean system with jumping balls
6 Stable running and long lifetime
7 Compact structure and less space required
1 Feeding crosswise— real-time regional control technology
2 Volume equal silo— ensure consistent bulk density
3 Aerodynamics— perfect balance of positive/negative pressure
airflow
4 Airflow regulation system— artful combination of vertical&
horizontal adjustment
5 Airflow surface forming— fine and smooth surface
6 Advanced control technology— high precision lengthwise and
crosswise density
1 Crosswise feeding— real-time regional control technology
2 More delicate diamond rollers— ensure forming precision
3 Positive/negative pressure assistant airflow— ensure better fine
surface
4 Core cage roller forming— uniform core mat structure
5 Advanced control technology— high precision lengthwise and
crosswise density
- Sanding and cut-to-size line